cycling performance

The effect of lithium polysulphides on the cyclic deposition/and dissolution of lithium metal on an inert stainless steel electrode and on a lithium metal electrode in sulfolane solutions has been studied. It has been shown that the addition of lithium polysulphides to sulfolane solutions leads to a significant increase in the cycle life (2 or more times) and cycling efficiency of a lithium metal electrode and a lithium metal on inert stainless steel electrode. It also results in the reduction of the corrosion rate of the lithium cathodic deposits.

Features of lithiated iron phosphate behavior (PH/P1, Phostech Lithium Inc, Canada) used as positive electrode of lithium-ion battery with LiPF₆-based electrolyte were investigated. It was shown that lihiated iron phosphate potential does not depend of lithium contents in active material. It was shown that cycle life of the positive electrode strongly depends on charge/discharge current. Fast degradation of the positive electrode takes place at low current rates (0.25 and 0.5C). At the same time degradation is considerably lower at 1 and 2.5C rates.