суперконденсатор

The possibility of using organic esters of phosphoric acid as a solvents for the electrolyte for lithium-ion systems and supercapacitors was investigated. Supercapacitors based on activated carbon Norit Supra and on the electrolyte being studied showed fine electrochemical performance which is comparable with standard electrolytes based on propylene carbonate. Lithium-ion batteries (Li4Ti5O12-LiNiO2 system) also showed a good performance.

There are the tests results of the symmetrical carbon super-capacitors (on the sulfuric acid electrolyte), whose electrodes are prepared with two methods (spraying and calendering) from two coals: coal of brand XH-00W1 (China) and coal, developed by the authors together with the Latvian state institute of wood chemistry. It is shown that the specific characteristics of super-capacitor substantially depend on the specific mass of electrodes (mg/sm2 ), and also from the method of their production.

The electrochemical behavior of carbon-fabric electrodes in the pristine state and after modification with titanium (magnetron sputtering), silver (chemical precipitation) and sequential titanium/silver coatings was studied. The effect of metallic coatings on the conductivity, permittivity, and dielectric losses of model symmetric supercapacitors–fabricated using carbon-fabric electrodes, both with and without the coatings– was investigated.

The electrical and chemical characteristics of nanocomposite materials based on carbon black for double-layer supercapacitors were investigated. It was shown that the highest values of the specific capacitive characteristics were obtained for carbon material SP4 which has the largest specific surface area (total capacity 228 F/g, reversible capacity 162 F/g).

In this paper we investigate carbon materials prepared from different organic raw materials of vegetable nature by the method of pyrolysis. Properties of obtained carbon substances are established by the methods of impedance spectroscopy, voltamperometry, and chronoamperometry. Starting from the data of electron paramagnetic resonance, impedance spectroscopy and an analysis of the Regon diagrams it is concluded that the obtained carbon materials contain carbon nanostructures in the form of bungles of multiwall nanotubes.

In this review electrochemical and structural data for the electrodes made of certain of perspective materials for supercapacitors are considered. These electrodes were made on the basis of high-dispersed carbon materials.

The efficiency of the electrolyte based on the mixture of acetonitrile – tetramethylammonium bis(oxalate)borate with the concentration of the latter 0.7 mol/kg in double layer supercapacitors has been shown. Electrochemical properties of active carbon materials Norit DLC Supra 30 and Kausorb-212 have been investigated in supercapacitor samples of disk construction in 2016 dimensions using potentiodynamic and galvanostatic methods.

In the current paper electrospun nanofiber mats were derived from polyacrylonitrile (PAN). The temperature influence on the volumetric and surface composition of the resulting pyropolymers was studied by means of elemental analysis and X-ray photoelectron spectroscopy.

We have studied the capacitance and kinetic properties of nanoporous carbon material which was obtained from wood. The maximum radius pore distribution of the investigated material was 1.37 nm. The data from X-ray scattering and electrochemical impedance spectroscopy was used to investigate the influence of porous structure change and electronic structure of activated carbon material on the mechanism and kinetics of charge-discharge at 7.6m KOH solution.

Behavior of electrodes based on activated carbon P2 (Ener G2) wih additions of plain carbon black, as well as carbon black doped with silver nanoparticles have been studied. Depending on potential range and polarization direction the electrodes were found to reveal a capacitance close to double-layer or pseudocapacitance.